玻璃容器的质量要求及抽验方案-曼谷玻璃公司.doc

玻璃容器的质量要求及抽验方案产品：630ml.Singha Beer1、 BOTTLE SPECIFICATION 玻璃瓶的规格PARAMETERS 检验项目STANDARDS 标准Bottle height (mm)瓶全高265.00±1.70Body diameter (mm)瓶身直径75.00±1.5Finish-A dia. (mm)瓶口外径26.5+0.3/-0.2Finish-B dia. (mm)环箍外径27.6±0.6Finish-C dia. (mm)？？18.50 (max)最大Dimension规格尺寸Finish-I dia. (mm)瓶口内径16.00 (min)最小Design weight (g-Approx)设计重量410Brimful capacity (ml)满口容量650Weight & capacity重量和容量Fillful capscity (ml)灌装线容量630±4.00Resistance to internal pressure (kg/cm2) 耐内压力20(avg),14 (min) 最小Resistance to thermal shock (diff.℃) 抗热震性42 (min) 最小Resistance to impact (ips) 抗冲击强度40 (min) 最小Resistance to vertical load (kg) 垂直荷重700 (min) 最小Physical property物理性能Annealing (temper no.) 退火应力3mm (diameter) 气泡>3mmStone 石头………………..Cold mould 凉模Fold of glass Lap mark 皱纹Loading mark 下料纹Washboard 搓板纹Swung baffle 闷头线偏Wedged bottom 偏底Blank seam 初模缝Mould seam 成模缝Offset mould seam 错缝Seed 灰泡………………..4、SAMPLING PLANS: SINGLE SAMPLING PLAN FOR NORMAL INSPECTION LEVEL Ⅱ抽验方案：对于一般检验水平的一次抽验方案Ref: MIL STD 105D 参照：MIL STD 105DAQL 0.015 %AQL 0.65 %AQL 2.50 % 批量样本量代码样本量 Ac ReAc ReAc Re1201-3200K1252 37 83201-10000L2003 410 1110001-35000M3155 614 1535001-150000N5007 821 22150001-500000P8000 110 11500001 及以上Q125014 15使用箭头下面第一个抽验方案使用箭头下面第一个抽验方案Ac 接受数Re 拒收数APPENDIX 附录DEFINITION OF CRITECAL DEFECTS 致命缺陷的定义CRETICAL DEFECTS 致命缺陷BIRDSWING:A thread of glass across the inside of a container.打：横联在玻璃瓶内部的玻璃丝。

FALSE BOTTLE: A large fin of glass extending from the inside surface, near an parallel to the base.假底：从瓶壁内侧伸出的一大块类似鱼翅状并且几乎与瓶底平行的玻璃INTERNAL FUSED BOTTLE: A piece of glass that has dropped inside a container while hot and stuck to the surface.内部粘玻璃：当玻璃灼热时掉入瓶里面并粘到玻璃瓶的内表面上的一片玻璃OVERPRESSED FINISH: Excessive glass projection upward from the inside of finish.口台：从瓶口内缘向上凸出的多余的玻璃SPIKE: A small projection of glass in the bottom of the container.瓶底凸出玻璃：瓶内底部凸出的一块玻璃STUCK PLUNGER: Raised needle of glass inside the finish.口内毛刺：瓶口内部凸出的玻璃刺LOOSE GLASS INTERNALLY: A piece of loose glass inside a container.瓶内游离玻璃：瓶内部的玻璃屑。

MAJOR DEFECTS 重要缺陷SPLIT FINISH：瓶口微裂纹 Differs from a crizzle sealing surface in that it is deep，not just on the skin of the glass, and commonly extends from the bore to the outside of the finish.不同于瓶口缝合面的裂纹，不但是在玻璃表面，经常是从里面向外延伸的瓶口裂纹 Blown out finish 口箍大：A finish where the walls are blown past vertical and bulge outwards.口箍的外缘被吹的凸出超过上限Chipped finish 口碎：A finish from which a small section is broken on the top of side.瓶口顶部边缘小块玻璃破碎Chipped thread 口丝碎:A thread of a container from which fragments of glass have been broken probably by impact.玻璃瓶的螺纹由于遭到撞击而破碎一部分Checked finish :炸口 A crack within the middle of the finish.瓶口中间的裂纹Checked thread: 揭丝 Checks occurring between the threads of any screw finish.出现在螺纹口的螺纹间的裂纹Unfilled finish 口不真: When the top of the ring is not completely filled up.瓶口顶部不完全饱满。

Line over finish 口平面条纹:A mark or line over the top sealing surface.瓶口密封面上的细条纹Offset finish 瓶口错位: A finish which is not correctly centered relative to the vertical axis of the neck.瓶口与脖颈的中心在一条垂直线上Body check 瓶身炸纹: A small but deep check where the hot glass has come into contact with a cold surface after forming, EG. Bare metal.在料胎从初型模成型以后，当热玻璃与冷表面(例如：金属)接触后产生的细而深的裂纹Hot mould check 瓶身炸纹: A check with a distinctive seagull or boomerang shape, usually occurring in the body panel.经常发生在瓶身贴标处的类似于海鸥状或者是回飞镖状的裂纹。

Pinched neck 卡脖: A distorted neck which has been unshed or pinched.玻璃瓶脖颈被挤压Split shoulder 揭膀: A fine vertical spilt on the shoulder area of a container.玻璃瓶肩部产生的垂直细裂纹Thin side 身薄: The container has an area of glass on the sidewall which is not thick enough to enable it to fulfill the purpose for which it was designed.玻璃瓶的瓶壁由于太薄不能达到设计的灌装功能Split seam 揭模缝：A vertical crack in the region forming at the seam between two parts of a mould.发生在模缝处的垂直裂纹Split bottom 炸底：Bottom in which a split occurs in any irection, but the spilt is usually radial.Thin bottom 瓶底薄: The bottom of the container has insufficient glass to allow it to fulfill the purpose for which it was designed.Over/under size body/height/weight/finish: 瓶身直径超标: Non-conforming to specification limits on body, height, weight, finish.Blister>3mm (diameter) 气泡>3mm: A blister is a cavity, build up of glass, within glass. The size of a blister that is usually objectionable is greater than 3mm in diameter.Stone 石: A small inclusion of refractory or unmelted batch materials.。