热机轧制实验方案+(1)+(1).docx

小棒线热机轧制（TMCP）实验方案一、 实验目的1、 改善轴承钢组织形态，降低退火消耗；2、 降低Cr、CrMo钢硬度；3、 细化晶粒、提高钢的强韧性；4、 冷镦钢热机轧制作为技术储备的工艺研究二、 实验钢种45、 40Cr、 20-42CrMoA、 GCr15 三、化学成分及相关数据钢种CSiMnPSCrNiCaMoTiCuAlSn450.450.260.650.0180.0090.10.100.020.02570.140.0150.0140Cr0.40.220.620.0150.0030.940.030.0010.010.00420.120.0150.01420CrMoA0.20.240.520.010.0030.920.010.00140.180.00180.070.0170.0130CrMoA0.30.220.510.010.0030.910.020.00140.180.00370.080.0160.01135CrMoA0.350.230.530.0140.0031.030.020.00140.180.00650.080.050.01242CrMoA0.420.250.760.0150.0031.040.020.00140.180.00430.080.0150.01420CrMnTi0.20.270.950.010.0051.150.020.00140.010.070.080.0290.01GCr1510.290.330.0130.0021.480.040.0010.010.00740.080.0170.012根据经验公式计算出相关钢种的奥氏体转变临界温度。

相关论文用公式：Ac1 = 723 - 26Si + 20Cr + 8W +16MO + 55V - 14Cu - 18Ni - 12MnAc3 = 910 - 320 C - 14Ni - 12Cu -10Mn + 5Cr + 7W + 14MO + 5V+18Si国内常用公式：Ac1 = 723 —14Mn%+22Si%—14.4Ni%+23.3Cr%Ac3 =854—180C%—14Mn%+44Si%—17.8Ni%—1.7Cr%钢种Ac1Ac3相关论文用 公式国内常用公 式参考值相关论文用 公式国内常用公 式参考值4570772172575977277040Cr72574274378478380520CrMoA73074374585282084030CrMoA73074375782080280735CrMoA73074375580479380042CrMoA73174473078177978020CrMnTi726742745846814830GCr15741759760900四、实验方案及过程控制参数1、试验材料的确定2、由技术中心与精棒分厂根据生产计划确定实验钢种及规格，进行 热机轧制试验，待参数调整达到设定值后，在4支坯所产材中间倍尺 上取样4 X400MM；，此规格热机轧制结束，水箱下线，产材取试料 后的钢材与未进行热机轧制钢材一起正常上交，不进行单独标识及管 理，同时取随后生产的同炉号未进行热机轧制钢材试料4 X400MM交 由技术中心检验；2、加热温度控制实验钢种在实验过程中加热温度按相应加热工艺的下限控制，以获得 细小而均匀的奥氏体晶粒，不允许高温长时间加热；3、控轧温度及控冷温度的确定钢种变形温度区间控轧温度轧制道次5#剪后温度45735-770°C760+10C4700+10C40Cr750-800°C780+10C4700+10C20CrMoA750-850C820+10C4700+10C30CrMoA760-820C800+10C4700+10C35CrMoA760-820C800+10C4700+10C42CrMoA750-800C780+10C4700+10C20CrMnTi750-850C820+10C4700+10CGCr15780-900C820±10C4710±10CGCr15 780-900°C | 820±10°C | 4 710±10°C4、不同规格各道次变形率规格1#减面率2#减面率3#减面率4#减面率总减面率16.020.522.814.55.450.217.017.518.712.54.543.818.013.115.110.84.437.019.08.512.19.24.129.820.05.57.87.63.622.220.08.511.48.53.928.621.019.120.914.25.247.922.514.616.911.64.540.224.08.613.410.54.031.926.04.06.97.63.420.126.08.510.58.24.027.628.017.520.013.74.545.630.013.015.011.74.537.532.08.511.19.14.028.934.04.05.97.63.919.834.07.010.59.34.127.536.017.621.114.04.746.738.014.417.012.44.540.640.010.013.911.24.434.242.56.99.48.34.025.742.510.012.710.34.432.645.017.621.315.24.647.548.014.516.212.94.540.350.011.513.311.74.435.25、水箱参数的设定使用CCT-OFFLINE，试轧前依据控轧控冷温度确定水箱参数。

根 据轧制过程中实际测定温度参数对水箱参数进行调整，直至达到试验 方案要求温度6、注意事项由于二段穿水，冷却强度大，钢材出2#水箱后表面温度低，易造成热检无信号，需对热检进行签定，必要时更换可进行低温检测热检五、 检验项目（试验钢与对比钢）1、 GCr15检验组织中珠光体片层间距，晶粒度及网状情况；2、 40Cr/35-42CrMo检验组织、晶粒度、机械性能及硬度；3、 45/20CrMnTi/20-30CrMo检验组织、晶粒度及机械性能六、 技术中心：负责试验方案的制定，试验过程的跟踪记录， 试料的检验分析、试验效果的评价精棒分厂：负责穿水水箱的上、下线，水缝开口度的标定、 工艺参数的控制、过程的记录、试料的切取。