英文文献信息检索方法和步骤013409108 陈真利用学校图书馆外文数据库 SpringerLink 进行英文文献检索的步骤：1、打开学校图书馆网页，点击数据库服务中的西文数据库，进入后再点击《Springer Link》数据库，进入SpringerLink数据库网页2、 进入SpringerLink数据库网页后，找到“Advanced Search”标志，点击后出 现一个界面框3、 在界面框中的"Content"下框中输入“Porous ceramic",再选择"Title Only"选择日期，先点击“Publication Dates Between",然后再设定日期为01/01/2010到 15/04/2012在“Order of Results"下面选择“Most Recently Published First"，然后点击“GO"4、 进入页面后将会出现很多英文论文，在第三页选择一篇名为“Preparation ofmullite bonded porous SiC ceramics by an infiltration method" 的文章，点击文 章题目进入5、 复制摘要，并点击“About”，得到有关文章的信息和该期刊的信息。

6、 摘要内容和翻译如下：Abstract :A powder compact of a-SiC and a-Al2O3 was infiltrated with a liquid precursor of SiO2, which on subsequent heat treatment at 1500 °C produced a mullite bonded porous SiC ceramics. Results showed that infiltration rate could be estimated by using weight gain measurements and theoretical analysis. The bond phase was composed of needle-shaped mullite which was observed to be grown from a siliceous melt formed during the process of oxide bonding. The porous SiC ceramics exhibited a density and porosity of 2 g.cm-3 and 30 vol%, respectively, and also a pore size distribution in a range of 2—15 pm with an average pore size of 5 pm. No appreciable degradation of room temperature flexural strength (51 MPa) was observed at high temperatures (1100 °C).翻译：题目：渗透法制备莫来石结合碳化硅多孔陶瓷摘要：用二氧化硅的液态先驱体渗透由a-碳化硅和a-氧化铝混合的粉饼， 然后放在1500°C的条件下进行热处理，就可以制备出莫来石结合的碳化硅的多 孔陶瓷。

实验结果表明，测量前后体重的增加量，并结合理论分析就可以估算出 渗透率的大小粘结相是由针状莫来石组成的，这些针状莫来石是在氧化物结合 的过程中由硅熔化形成的碳化硅多孔陶瓷的密度和孔隙度分别为2g.cm-3和 30vol%,孔径的大小分布在2-15pm之间，平均孔径为5pm陶瓷的抗折强度 (51Mpa)在室温和在高温下(1100C )相比没有明显的差距7、有关文章的信息和该期刊的信息如下：About This ArticleTitlePreparation of mullite bonded porous SiC cermaiscs by an infiltration method Authors• Atanu Dey(1)• Nijhuma Kayal(1)• Omprakash Chakrabarti(1)omprakash@cgcri.res.inAuthor Affiliations1. Non-Oxide cermaiscs and Composites Divisions, Central Glass andcermaisc Research Institute, Council of Scientific and Industrial Research, 196, Raja S. C. Mullick Road, Kolkata, 700 032 IndiaDOI10.1007/S10853-011-5484-XSpringerLink DateFriday, April 01, 2011About This JournalTitleJournal of Materials ScienceCoverageVolume 1 / 1966 - Volume 47 / 2012CollectionChemistry and Materials ScienceSubjects• Chemistry• Materials Science• Characterization and Evaluation Materials• Polymer Sciences• Continuum Mechanics and Mechanics of Materials• Crystallography• MechanicsISSN0022-2461 (Print)1573-4803 (Online)Additional Links• Register for TOC Alerting• Editorial Board• About This Journal• Manuscript SubmissionPublisherSpringer NetherlandsSpringerLink DateFriday, April 05, 2002。