协羽管道技术资料.doc

协 羽 管 道 技 术 资 料(一)UPVC,CPVC,SCH80 管尺寸与压力定律 ◎ Schedule 80 size Average outer diameter minimum thickness working water pressure minimum demolition hydraulic pressure inch Nominal diameter mm mm psi(kg/cm2) psi(kg/cm2)1/2" 15 21.3 3.7 850(59.8) 2720(191.4)3/4" 20 26.7 3.9 690(48.5) 2200(154.8)1" 25 33.4 4.6 630(44.3) 2020(142.2)1+1/4" 32 42.2 4.9 520(36.6) 1660(116.8)1+1/2" 40 48.3 5.1 470(33.1) 1510(106.8)2" 50 60.3 5.5 400(28.2) 1290(90.8)2+1/2" 65 73.0 7.1 420(29.6) 1360(95.7)3" 80 88.9 7.6 370(26.0) 1200(84.4)4" 100 114.3 8.6 320(22.5) 1040(73.2)6" 150 168.3 11.0 280(19.7) 890(62.6)8" 200 219.1 12.7 250(17.6) 790(55.6)10" 250 273.1 15.1 230(16.2) 750(52.8)12" 300 329.9 17.5 230(16.2) 730(51.4)◎ Schedule 40size Average outer diameter minimum thickness working water pressureminimum demolition hydraulic pressure inch Nominal diameter mm mm psi(kg/cm2) psi(kg/cm2)1/2" 15 21.3 2.77 600(42.2) 1910(134.4)3/4" 20 26.7 2.87 480(33.8) 1540(108.4)1" 25 33.4 3.38 450(31.7) 1440(101.3)1+1/4" 32 42.2 3.56 370(26.0) 1180(83.0)1+1/2" 40 48.3 3.68 330(23.2) 1060(74.6)2" 50 60.3 3.91 280(19.7) 890(62.6)2+1/2" 65 73.0 5.16 300(21.1) 970(68.3)3" 80 88.9 5.49 260(18.3) 840(59.1)4" 100 114.3 6.02 220(15.5) 710(50.0)6" 150 168.3 7.11 180(12.7) 560(39.4)8" 200 219.1 8.18 160(11.3) 500(35.2)◎ UPVC temperature damping constant 工作温度℃23 27 32 38 43 49 54 60温度递减常数1.00 0.88 0.75 0.62 0.51 0.40 0.31 0.22◎ CPVC temperature damping constant 工作温度℃23-26.7 32 38 49 60 66 71 77 82 88 93 99温度递减常数1.00 0.92 0.82 0.65 0.50 0.47 0.40 0.32 0.25 0.22 0.20 0注：1.1kg/cm2 =14.223psi 1Mpa=142.86psi 1BAR=14.5PSI=0.9869 大气压 1psi=6.9kpa2..以上压力定律适用于水温 23℃,当温度高于 23℃时，须视其材料（UPVC 或 CPVC) 乘以上列温度递减常数。

而水以外流体之压力定律并不全然适用上表3.采用法兰接合处之工作压力建议不应超过 150psi(10kg/cm2),而利用螺纹（牙口）接合处之工作压力建议不应超过该尺寸对应工作压力之 50%.4.CPVC 螺纹在流体温度 66℃以上时不建议使用5.全尺寸 SH40 管及 6"以上 SC H80"管建议不可加螺纹6.协羽牌 CPVC FG SCH40 1/2"尺寸热水管经 “国家化学建材测试中心”测试，水温在 23±2℃时，管材爆破压力高达 19.5Mpa (195.9kg/cm2)协 羽 管 道 技 术 资 料（二）材质 简称 一般化学性能 最高工作温度长时间 短暂聚氯乙烯 PVC可耐大部分的“酸” 、“ 碱”、“盐”由低到高浓度的腐蚀，但不耐“芳香烃”、“酮” 、“醚”、“氯化碳烃类” 腐蚀55℃ 60℃氯化聚氯乙烯CORZAN CPVC耐化学腐蚀性与 PVC 相似，仅耐温性比PVC 好 95℃ 110℃聚丙烯 PP耐化学性非常好，对一般的酸的抵抗性也好，唯较不耐两种不同酸的混合液，如：硝酸＋硫酸或硫酸＋氢氟酸对一般有机溶剂90℃ 110℃聚二氟乙烯 PVDF 耐化性非常好，只会被“发烟硫酸、三氧化硫、强碱胺类、酮类“等腐蚀。

140℃ 150℃聚四氟乙烯（铁氟龙） PTFE几乎不被任何化学药品腐蚀，只有在高温下才会被少数化学药品腐蚀 250℃ 300℃氟橡胶（氟化乙烯与 六氟化丙烯的共聚物） VITONFPM耐侯性、耐臭氧、耐油、耐热性、耐化学药品性均好是自熄性橡胶，但耐寒性不好（-45℃脆化点）200℃ 200℃乙烯丙烯橡胶 EPDM耐侯性、耐臭氧、耐化学药品性优，耐油性好，是自熄性橡胶，耐低温性差，不耐芳香烃类90℃ 120℃丁二烯腈橡胶（BUNNA-N) NBR 主要效能是“耐油性好”，耐热性佳，在120℃可长期使用，耐寒性差，耐水性差 120℃ 120℃协羽管道技术资料（三）UPVC/CPVC 管材及管件施工方法说明 协羽技术资料（四）耐药品性一览表1) ★ 不侵蚀（使用良好） Non-Corrosive(good in use)(2) ● 大致不侵蚀（可以使用）Very Slihly Corrosive(usable)(3) ▲ 稍微侵蚀（视情形而使用）Slightly Corrosive(according to situations)(4) X 侵蚀（不可使用）Corrosive(not usable)Table of Reagents-Resistant CharactorPVC(℃) PP(℃) PPG(℃ )FRTP PVFD(℃) PTEE(℃ )Teflon EPDM(℃) CR(℃)Neoprene CSM(℃ )hypalon FPM(℃)Viton 药品 Reagents\分类 Category 20 40 60 30 60 90 30 60 120 30 90 130 120 180 260 20 60 110 20 40 80 20 40 90 60 120 180监酸 Hydrochloric Acid 36% 144g 混★ ★ ● ★ ★ ● ★ ★ ● ★ ● ● ★ ● ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ● ●硫酸 Sulfuric Acid 98% 13g Mixture★ ★ ● ★ ★ ● ★ ★ ● ★ ● ● ★ ● ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ● ●监酸 Hydrochloric Acid 20% 100g 混★ ★ ● ★ ● ● ★ ● ● ★ ● ● ★ ● ▲ ★ ● ● ★ ● ● ★ ★ ● ★ ● ●硫酸 Sulfuric Acid 5% 5g Mixture★ ★ ● ★ ● ● ★ ● ● ★ ● ● ★ ● ▲ ★ ● ● ★ ● ● ★ ★ ● ★ ● ●监酸 Hydrochloric Acid 20% 100g 混★ ★ ● ★ ● ▲ ★ ● ▲ ★ ● ▲ ● ● ▲ ★ ▲ ▲ ★ ● ▲ ★ ● ● ★ ● ▲硝酸 Nitric Acid 50% 5gr Mixture ★ ★ ● ★ ● ▲ ★ ● ▲ ★ ● ▲ ● ● ▲ ★ ▲ ▲ ★ ● ▲ ★ ● ● ★ ● ▲对笨二甲酸 Nickel Sulphate, 20%★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★对笨二甲酸 Nickel Sulphate, 50%★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★硫酸镁 Magnesium Sulphate, 稀释★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★硫酸镁 Magnesium Sulphate, 100%★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★氯化第一铁 Ferrous Chloride 5% 混合★ ★ ● ★ ● ● ★ ● ● ★ ● X ● ● X ★ ● ● ★ ● ● ★ ★ ● ★ ● ▲氯化第二铁 Ferrous Chloride 5% 混合★ ★ ● ★ ● ● ★ ● ● ★ ● X ● ● X ★ ● ● ★ ● ● ★ ★ ● ★ ● ▲苹果酸 Apple Acid 1% ★ ★ ● ★ ★ ● ★ ● ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ★砷酸 Arsenic Acid (稀释 Diluted)★ ★ ● ★ ★ ★ ★ ★ ● ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ X ★ ★ X ★ ★ ★砷酸 Arsenic Acid (稀释 Diluted 80%)★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★苯醛 Benzaldehyde 0.1%★ ● X ★ ▲ X ★ ● X ★ ● X ★ ● ▲ ★ ★ ● ★ ● ★ ★ ● ★ ★ ●苯 Benzene, 工业纯净 Technically Pure▲ ▲ X ▲ ▲ X ▲ ▲ X ● ▲ X ● ▲ X ▲ ▲ X ▲ ▲ X ▲ ▲ X ★ ● X苯和石油精 Benzine Benzene 80%▲ ▲ X ▲ ▲ X ▲ ▲ X ● ▲ X ● ▲ X ▲ ▲ X ▲ ▲ X ▲ ▲ X ★ ● X酒精 Benzyl Alcohol 100% ★ ● ● ★ ● ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ● ● ★ ● ● ★ ● ● ★ ● ●硼砂 Borax, 稀释 Diluted ★ ★ ● ★ ★ ● ★ ★ ★ ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ★硼酸 Boric Acid (稀释 Diluted) ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ● ★ ★ ★溴 Bromine 液体 100% ▲ ▲ X ▲ ▲ X ▲ ▲ X ● ▲ X ● ▲ X ▲ ▲ X ▲ ▲ X ★ ▲ X ★ ▲ X溴 Bromine, 水蒸气少量 Vapours Poor● ▲ X ● ▲ ● ● x ● ● ▲ ● ● ▲ x ● ▲ x ▲ ▲ x ★ ● ★ ● ▲溴 Bromine, 水饱和 Water Saturated★ ▲ x ▲ ▲ x ● ▲ x ★ ● ▲ ★ ● ▲ ● ▲ ▲ ▲ ★ ● ▲ ★ ● ▲丁二烯 Buaddiene 50% ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ● ▲ ★ ★ ● ● ● ▲ ★ ● ●丁二烯 。