文献汇报,黄智,2011.10.22,Received February 17, 2010; E-mail: hailiangzhang@; eqchen@,Hierarchical Supramolecular Ordering with Biaxial Orientationof a Combined Main-Chain/Side-Chain Liquid-CrystallinePolymer Obtained from Radical Polymerization of2-Vinylterephthalate,Key Laboratory of Polymeric Materials and Application Technology of Hunan Pro ince and KeyVLaboratory of Ad anced Functional Polymer Materials of Colleges and Uni ersities of HunanV VPro ince, College of Chemistry, Xiangtan Uni ersity, Xiangtan 411105, Hunan Pro ince, China,V V Vand Beijing National Laboratory for Molecular Sciences, Department of Polymer Science andEngineering, and Key Laboratory of Polymer Chemistry and Physics of the Ministry ofEducation, College of Chemistry and Molecular Engineering, Peking Uni ersity,VBeijing 100871, China,研究背景与意义,主/侧链结合型液晶高分子具有主链液晶高分子和侧链液晶高分子的结构特点，主链和侧链存在相互作用，其相行为和相结构很复杂，对其研究也是相当有限的。

此类聚合物是通过缩合聚合的方法合成，很难获得结构规整、分子量可控、分布较窄的聚合物，阻碍了此类液晶聚合物的进一步研究研究背景与意义,主链：甲壳型液晶高分子,侧链：含联苯液晶基元的侧链型液晶高分子,研究背景与意义,运用ATRP方法合成了一系列不同分子量、窄分布的主/侧链结合型液晶高分子 分子量小得样品PBBHCS-1表现出普通侧链型液晶聚合物的性质，在不同温度下经历不同的相行为：各向同性 近晶A 近晶B 近晶E；分子量较大的样品由于甲壳型刚性主链和侧链联苯液晶基元的相互作用，表现出更为复杂的相行为：各向同性 近晶A 熔融的侧链联苯液晶基元与刚性主链形成的长方形二维纳米框架结构相结合成双轴取向有序超分子结构 侧链联苯液晶基元形成近晶E的结构与刚性主链形成的长方形二维纳米框架结构相结合成双轴取向、双层次的有序超分子结构 分子量越大主链形成的纳米级的框架结构越稳定 侧链联苯液晶基元具有偶极矩，在外加电场作用下能取向，从而带动整个聚合物的宏观取向不同升温速率的DSC实验,三个明显的相转变观察不到玻璃化转变说明主链与侧链协调作用形成了高度有序的超分子结构,变温的1D WAXD实验,Figure 2. Set of 1DWAXD powder patterns of1(Mn=1.55×10 g/mol))recorded upon cooling at various temperatures.,①,180℃高角区只有一个较宽的弥散峰 无定形态,②,170℃，低角区出现两个个衍射峰，形成了层状相，高角区仍然是弥散衍射包 低级有序的近晶A相,③,164 ℃低角区出现四个新的衍射 次级纳米短程有序结构,④,163℃-162℃，过渡状态,⑤,160℃-140℃，低角区两个峰消失，四个峰仍然保留 纳米有序结构稳定存在,⑥,到125℃，低角区四个峰明显变化，高角区出现三个尖锐的衍射峰 两套不同尺度的有序结构,2D WAXD实验,刚性主链直径计算,高分子量样品电场取向行为研究,1.温度低于低温相转变温度时即使加上很强电场，织构仍然保持不变2.超过140℃，即低温相转变，联苯液晶基元熔融 零界电压3.升温到第二个相转变温度，极低电压都可以观察到明显的织构变化,分子量大小对聚合物的影响,分子量小于1.0×104g/mol时，主链不能形成甲壳型刚性结构，表现出普通侧链型液晶高分子的性质 分子量足够的高分子样品表现出主 /侧链结合液晶高分子的性质。

Thank you!,,。