台化abs物性.doc
2页
TAIRILAC ABS resin consolidated property data sheet項 目Property單 位Unit試驗方法Test Method試驗條件Test ConditionAG15E1 抗張強度Tensile Strengthkg/cm2( MPa)ASTM D-638( ISO527)23℃530(52) 彎曲強度Flexural Strengthkg/cm2( MPa)ASTM D-790( ISO178)23℃870(86) 彎曲模數Flexural Moduluskg/cm2( MPa)ASTM D-790( ISO178)23℃28000(2750) 洛式硬度Rockwell HardnessR-ScaleASTM D-785( ISO2039/2 )23℃R-110Izod 衝擊強度Izod Impact Strengthkg-cm/cm( J/m )ASTM D-256( ISO R180 )23℃ 1/4'' 厚14(137) 衛氏軟化點Vicat Softening Point℃ASTM D-1525(ISO 306)1 Kg Load103Unannealed18.6kg/cm2 ( 1/2'' 厚 )88熱變形溫度Heat DeflectionTemperature℃ASTM D-648(ISO 75/A)Annealed18.6kg/cm2( 80 ℃×8Hr)100200℃×5Kg( 49N )1.8熔融指數Melt Flow Indexg/10 minASTM D-1238( ISO1133 )220℃×10Kg( 98N )20收縮率Molding Shrinkage%FCFCMethod23℃0.4~0.7比 重Specific GravityASTM D-792( ISO1183 )23℃/23℃1.05燃燒性FlammabilityUL-94FILE NO.E1628231/16“ HBAll ColorTAIRILAC ABS resin consolidated property data sheet項 目Property單 位Unit試驗方法Test Method試驗條件Test ConditionAG15A1 抗張強度Tensile Strengthkg/cm2( MPa)ASTMD-638( ISO527)23℃510(50)彎曲強度Flexural Strengthkg/cm2( MPa)ASTMD-790( ISO178)23℃850(84)彎曲模數Flexural Moduluskg/cm2( MPa)ASTMD-790( ISO178)23℃27000(2650)洛式硬度RockwellHardnessR-ScaleASTMD-785( ISO2039/2 )23℃R-110Izod 衝擊強度IzodImpact Strengthkg-cm/cm( J/m )ASTMD-256( ISO R180 )23℃ 1/4'' 厚20(196)衛氏軟化點Vicat Softening Point℃ASTMD-1525(ISO 306)1 Kg Load104Unannealed18.6kg/cm2 ( 1/2'' 厚 )89熱變形溫度Heat DeflectionTemperature℃ASTMD-648(ISO 75/A)Annealed18.6kg/cm2( 80 ℃×8Hr)101200℃×5Kg( 49N )1.6熔融指數Melt Flow Indexg/10 minASTMD-1238( ISO1133 )220℃×10Kg( 98N )17收縮率Molding Shrinkage%FCFCMethod23℃0.4~0.7比 重Specific GravityASTMD-792( ISO1183 )23℃/23℃1.05燃燒性FlammabilityUL-94FILE NO.E1628231/16“ HBAll Color。