常用塑料物性.docx

性 能LDPELLDPEHDPE相对密度0.91~0.930.92~0.9250.92~0.97吸水率/%<0.01<0.01<0.01成型收缩率/%1.5~5.01.5~5.52.0~5.0拉伸强度/MPa7~1515~2521~37断裂伸长率/%>650>880>500弯曲弓S度/MPa34一11压缩弓虽度/MPa28一10缺口冲击强度/(kJ/m2)80~90>7040~70洛氏硬度R45一R70热变形温度(1.86MPa)/C507578脆化温度/C-80~-55<-120<-140~-120线膨胀系数/( 10—5K-1)20~24一12~13热导率/[W/(m K)]0.35一0.44体积电阻率/Qcm6X1015一6X1015介电常数(106Hz)2.28~2.32一2.34~2.38介电损耗角正切值(106Hz)0.0003一0.0003介电弓虽度/(kV/mm)>20一>20耐电弧/s115一115氧指数/%20一20性 能通用软PVC电器用软PVC硬PVC相对密度l.2~1.61.2~1.61.4~l.6吸水率/%0.250.15~0.750.07~0.4成型收缩率/%1.5~2.51.5~2.50.6~1.0拉伸弓S度/MPa10.5~20.l10.5~20.l45.7断裂伸长率/%100~500100~50025弯曲弓S度/MPa一一100弯曲才11量/MPa一一3000压缩弓虽度/MPa8.88.820.5缺口冲击强度/(kJ/m2)一一2.2~10.6邵氏硬度A50~95A60~95D75~85长期使用温度/C60~7080~10480~90线膨胀系数/( 10—5K-1)7~257~255~18.5热导率/[W/(m K)]0.150.150.16体积电阻率/Q cm1011~1013101l~10141012~1014介电常数(106Hz)5~94~53.2~3.6介电损耗角正切值(106 Hz)0.08~0.150.08~0.150.02介电弓S度/(KV/mm)14.7~29.526.59.85~35耐电弧/s一60~80一性能数据性 能数据相对密度0.90热变形温度(1.82MPa)/ C102吸水率/%0.01脆化温度/C-8~8成型收缩率/%1~2.5线膨胀系数/( 10-5K-1)6~10拉伸强度/MPa29热导率/[W/(m K)]0.24断裂伸长率/%>200体积电阻率/Q cm1019弯曲弓S度/MPa50介电常数(106Hz)2.15压缩弓虽度/MPa45介电损耗角正切值(106Hz)0.0008缺口冲击强度/(kJ/m2)0.5介电弓虽度/(kV/mm)24.6洛氏硬度R80~110耐电弧/s185摩擦因数0.51氧指数/%18磨痕宽度/mm10.4性 能数据性 能数据相对密度1.05维卡软化点/C100吸水率/%0.05长期使用温度/C60~75成型收缩率/%0.4~0.7脆化温度/c-30透光率/%88~92线膨胀系数/( 10-5K-1)8折射率1.59~1.60热导率/[W/(m K)]0.14拉伸强度/MPa50体积电阻率/Q cm1017~1019断裂伸长率/%2介电常数(106Hz)2.45~2.65弯曲弓S度/MPa105介电损耗角正切值(106 Hz)(1~2) W-4压缩弓虽度/MPa115介电弓虽度/(kV/mm)20~28弯曲弹f4模量/MPa3200耐电弧/s60~l35无缺口冲击强度/(kJ/m2)16氧指数/%20洛氏硬度M65~90性 能高抗冲型耐热型中抗冲型相对密度1.02~1.051.06~1.081.05~1.07吸水率/%0.2~0.450.2~0.450.2~0.45成型收缩率/%0.3~0.80.3~0.80.3~0.8拉伸强度/MPa35~4445~5742~62断裂伸长率/%5~603~205~25弯曲弓S度/MPa52~8170~8569~72压缩弓虽度/MPa49~6465~7173~88悬臂梁缺口冲击强度/(J/m)16~4411~256~22洛氏硬度R65~109R105~115R108~115热变形温度(1.82MPa)/ C93~103104~11893~107线膨胀系数/(彳0—5K—1)9.5~10.56.0~9.05~8.5热导率/[W/(m K)]0.16~0.290.16~0.290.16~0.29体积电阻率/ Q cm(1~4.8) 1016(1~5) 1016(1~5) 1016介电常数(106Hz)2.4~3.82.4~3.82.4~3.8介电损耗角正切值(106Hz)0.0090.0090.009介电弓虽度/(kV/mm)13~2013~2013~20耐电弧/s66~8266~8266~82氧指数/%202020表2-22 ACS的主要性能性 能通用级阻燃级性 能通用级阻燃级相对密度1.071.16介电弓虽度/(mV/m)2625.4拉伸弓S度/MPa31.3639.2体积电阻率/Q cm2X10157.3d断裂伸长率/%4050介电常数(103 Hz)3.23.05冲击弓S度/(J/m)490117.6氧指数/%一28.5热变形温度「C8678成型收缩率/%0.40.4性 能PA6PA66PA1010PA610PA11PA12相对密度1.141.141.051.081.04~1.061.01~1.03吸水率/%3.0~4.23.4~3.61.51.8~2.01.050.25成型收缩率/%0.6~1.60.8~1.51.0~1.51.21.20.3~1.5拉伸强度/MPa7480556055~6255~64断裂伸长率/%20060250200300250~300洛氏硬度M114M118M116M95M108M106Izod冲击强度/(J/m)564040~50563852~116长期使用温度/C105105一806055热变形温度/C7075一5752一热导率/[W/(m-K)]0.280.240.16~0.40.220.29一线膨胀系数/(炉心6.57一811一介电常数(10 3 Hz)3.83.93.63.63.74.5体积电阻率/Q cm5X10137X10144X10144X10144X10138X1014介电强度 /(kV/mm)181510~15181715介电损耗角正切值(10 6Hz)0.020.020.020.02一0.03性 能PC30%玻璃纤Zt增强PC相对密度1.21.45吸水率/%0.150.1成型收缩率/%0.50.2拉伸强度/MPa56~66132拉伸模量/MPa2100~240010000断裂伸长率/%60~120<5弯曲弓S度/MPa80~85170弯曲才11量/MPa2100~2440一压缩弓虽度/MPa75~80120~130剪切强度/MPa35一缺口冲击强度/(kJ/m2)17~248洛氏硬度M80M90疲劳极限106次/MPa10.5一热变形温度(1.82MPa)/ C130~135146长期使用温度/C110130线膨胀系数/( K05K-1)7.22.7热导率/[W/(m K)]0.20.13体积电阻率/Q cm2.1 X0161.5 X016介电常数(106Hz)2.93.45介电损耗角正切值(106Hz)0.00830.0070介电弓虽度/(kV/mm)1819耐电弧/s120120性能指标均聚POM共聚POM25%GF 共 POM相对密度1.431.411.61吸水率/%0.250.21一成型收缩率/%1.5~31.5~3.5一拉伸强度/MPa7062130断裂伸长率/%4060一拉伸模量/MPa316028308300弯曲弓S度/MPa9098182弯曲才11量/MPa288026007600压缩弓虽度/MPa127110一剪切强度/MPa6754一缺口冲击强度/(J/m)766586洛氏硬度M94M80一摩擦因数一0.15一疲劳极限/MPa3531一热变形温度(1.82MPa)/C110124l63长期使用温度/C80100一线膨胀系数/( 10—5K—1)7.58.52.6热导率/[W/(m K)]0.230.23一体积电阻率/Q cm101510153.8 1014介电常数(106Hz)3.82.7一介电损耗角正切值(106Hz)0.0050.007一介电弓虽度/(kV/mm)2020一耐电弧/s220240一性 能电妒BT30%GFPBT阻燃增强PBT相对密度1.311.531.67吸水率/%0.090.070.07成型收缩率/%一0.5~1.00.5~1.2拉伸弓S度/MPa55137137断裂伸长率/%200~30044弯曲弓S度/MP。