DIC 水性环氧树脂 EN 201611资料
COPYRIGHT DIC CORPORATION ALL RIGHTS RESERVED EPICLON Waterborne epoxy resin Polymer Tech Group 1 Polymer Tech Div 1 DIC Corporation Rev 3 2016 11 EPICLON 1K Waterborne epoxy resinEPICLON 1K Waterborne epoxy resin Product name EPICLON HProduct name EPICLON H 502502 42W New Product 42W New Product launched in China in May 2016 launched in China in May 2016 1K coatings forced drying 1K coatings forced drying UsagesUsages Anticorrosion coatings Metal primer coatingsAnticorrosion coatings Metal primer coatings Top featuresTop features High anticorrosion performance Good High anticorrosion performance Good adhesion for metalsadhesion for metals COPYRIGHT DIC CORPORATION ALL RIGHTS RESERVED 2 EPICLON 2K Waterborne epoxy resin Amine Hardener EPICLON 2K Waterborne epoxy resin Amine Hardener Product name EPICLON EMProduct name EPICLON EM 101101 56 New Product 56 New Product launched in China in Oct 2016 LUCKAMIDE EXClaunched in China in Oct 2016 LUCKAMIDE EXC 1270 pilot scale 1270 pilot scale 2K Coatings air drying 2K Coatings air drying UsagesUsages Anticorrosion coatingsAnticorrosion coatings Bridge Tunk Pipe Bridge Tunk Pipe Container etc Container etc Top featuresTop features Anticorrosion performanceAnticorrosion performance COPYRIGHT DIC CORPORATION ALL RIGHTS RESERVED 3 Manufacturing locationManufacturing location JapanJapan DICDIC KitanihonKitanihon polymerpolymer in Miyagi WB Epoxyin Miyagi WB Epoxy Chiba Plat Epoxy HardenerChiba Plat Epoxy Hardener ChinaChina DIC DIC ZhangjiagangZhangjiagang Chemicals WB EpoxyChemicals WB Epoxy COPYRIGHT DIC CORPORATION ALL RIGHTS RESERVED 4 COPYRIGHT DIC CORPORATION ALL RIGHTS RESERVED 5 BCS Butyl cellosolve IPA Isopropyl alcohol DMEA 2 Dimethylamino ethanol OO OH OO n OH OH OO OH OO n OH OH Modified epoxy resin No epoxy group is left Ave particle size 0 1 0 3 High anticorrosion performance Good pigment dipersibility Good storage stability Top features Anticorrosion coatings Marine coatings General coatings Usages Registration ENCS Japan Listed IECSC China Simplified Notification Typical properties Appearance Milky liquid Viscosity 25 4500 mPas Non Volatile content 41 0 Solvent Resin Water BCS IPA DMEA 41 41 17 1 4 6 8 10 none Frequency Dense D Medium dense MD Medium M Few F Test results 1 component system clear COPYRIGHT DIC CORPORATION ALL RIGHTS RESERVED 7 Salt spray test 300h Reference Water based Solvent based H 502 42W COPYRIGHT DIC CORPORATION ALL RIGHTS RESERVED 8 H 502 42W Remarks Drying condition 23C20min 140C20min 23C20min 100C20min 23C20min 60C20min 23C1week 23C1week Dry film thickness m 30 30 30 30 Cross cut test 100 100 100 100 100 100 1mm 1mm DuPont impact Pass Pass Pass Pass 1kg 50cm Pencil hardness 2H H H H Solvent resistance 10 times 10 times 10 times 10 times MEK rub test Load 500g Water resistance Degree of blistering Good 10 Good 10 Good 10 Poor 10 blushing Dipping test 40C 7days Salt spray test Degree of blistering Peeling test width Good 10 2 mm Good 10 3 mm Good 10 3 mm Poor 10 blushing 4 mm 300hrs Coating condition Clear coating Substrate Cold rolled steel SPCC SD Coating method Bar coater Degree of blistering Size 2 4 6 8 10 none Frequency Dense D Medium dense MD Medium M Few F Effects of drying conditions COPYRIGHT DIC CORPORATION ALL RIGHTS RESERVED 9 Material Supplier Weight Remarks Disperse 1 4 50g of glass beads with sand mill for 30 min then add 5 and stir for 5 min 1 Disperbyk 190 BYK 3 0 Dispersant 2 Ti pure R 706 Dupont 60 0 Titanium dioxide 3 SN Defoamer 777 San Nopco 0 3 Defoamer 4 Deionized water 20 0 5 H 502 42W DIC 142 9 NV 42 0 Total 226 2 PWC 50 Recommended formulation for 1 component system COPYRIGHT DIC CORPORATION ALL RIGHTS RESERVED 10 H 502 42W Remarks Dry film thickness m 30 Cross cut test 100 100 100 1mm DuPont impact 300g 50cm 1kg 50cm Pencil hardness H Solvent resistance 10 times MEK rub test Load 500g Water resistance Degree of blistering Good 10 Dipping test 40C 7days Salt spray test Degree of blistering Peeling test width Good 10 3 mm 300hrs Coating condition Substrate Cold rolled steel SPCC SD Coating method Bar coater Curing condition 23C20min 140C20min Degree of blistering Size 2 4 6 8 10 none Frequency Dense D Medium dense MD Medium M Few F Test results 1 component system enamel COPYRIGHT DIC CORPORATION ALL RIGHTS RESERVED 11 NV H 502 42W REF Solvent based modified epoxy EPICLON H 502 42W 42 0 214 3 solid 90 0 WATERSOL S 695 66 0 15 2 solid 10 0 Solvent based modified epoxy 45 0 200 0 solid 90 0 Solvent based methylated melamine 60 0 16 7 solid 10 0 BECKAMINE P 198 0 3 0 3 Thinner If necessary If necessary Recommended formulation for 2 component system Formulation Modified epoxy melamine resin catalyst 90 10 0 3 solid solid soln DIC s product Type Non Volatile content Recommended usage Curing agent WATERSOL S 695 Waterborne methylated melamine 66 0 5 20wt H 502 42W solid solid Catalyst BECKAMINE P 198 Acid 0 1 1 0wt resin solution solid COPYRIGHT DIC CORPORATION ALL RIGHTS RESERVED 12 H 502 42W S 695 P 198 REF Sol